[1]鄭明毅,徐超,喬曉光,等.超高強韌Mg-Gd-Y-Zn-Zr變形鎂合金研究進展[J].中國材料進展,2020,(1):019-30.[doi:10.7502/j.issn.1674-3962.201908036]
ZHENG Mingyi,XU Chao. QIAO Xiaoguang,SUN Wanting,et al.Research Progress on UltraHigh Strength and Toughness Mg-Gd-Y-Zn-Zr Wrought Magnesium Alloys[J].MATERIALS CHINA,2020,(1):019-30.[doi:10.7502/j.issn.1674-3962.201908036]
點擊復(fù)制
超高強韌Mg-Gd-Y-Zn-Zr變形鎂合金研究進展(
)
中國材料進展[ISSN:1674-3962/CN:61-1473/TG]
- 卷:
-
- 期數(shù):
-
2020年第1期
- 頁碼:
-
019-30
- 欄目:
-
- 出版日期:
-
2020-01-31
文章信息/Info
- Title:
-
Research Progress on UltraHigh Strength and Toughness Mg-Gd-Y-Zn-Zr Wrought Magnesium Alloys
- 文章編號:
-
1674-3962(2020)01-0019-12
- 作者:
-
鄭明毅; 徐超; 喬曉光; 孫婉婷; 池元清
-
(哈爾濱工業(yè)大學(xué)材料科學(xué)與工程學(xué)院,黑龍江,哈爾濱,150001)
- Author(s):
-
ZHENG Mingyi; XU Chao. QIAO Xiaoguang; SUN Wanting; CHI Yuanqing
-
(School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China)
-
- 關(guān)鍵詞:
-
超高強鎂合金; 稀土; 顯微組織; 強韌化; 變形鎂合金
- Keywords:
-
ultrahigh strength Mg alloys; rare earth; wrought Mg alloys; microstructure; strengthening and toughening
- 分類號:
-
TG146.22
- DOI:
-
10.7502/j.issn.1674-3962.201908036
- 文獻標(biāo)志碼:
-
A
- 摘要:
-
超高強韌鎂合金的研發(fā)對推廣鎂合金在高技術(shù)領(lǐng)域的應(yīng)用具有重要意義。鎂與稀土均是我國的優(yōu)勢資源,因此在我國發(fā)展超高強韌稀土鎂合金具有得天獨厚的優(yōu)勢,其中Mg-Gd-Y-Zn-Zr系變形鎂合金因其接近高強鋁合金的超高強度和塑性,近年來受到研究者的廣泛關(guān)注。綜述了超高強韌Mg-Gd-Y-Zn-Zr系變形鎂合金的合金成分、常規(guī)塑性變形工藝、新型劇烈塑性變形工藝和熱處理工藝對該合金顯微組織和力學(xué)性能的影響規(guī)律,以及該超高強韌變形鎂合金的顯微組織特征和強韌化機理。T5峰時效態(tài)超高強韌Mg-8-2Gd-3-8Y-1Zn-0-4Zr(質(zhì)量分數(shù))擠壓合金具有雙峰分布的晶粒尺寸“軟-硬”復(fù)合層片微結(jié)構(gòu),以及由高密度的基面γ′納米片狀析出相和棱柱面β′納米析出相形成的近連續(xù)網(wǎng)狀結(jié)構(gòu),該擠壓合金室溫拉伸屈服強度、拉伸強度和斷裂延伸率分別為466 MPa、514 MPa和14.5%。介紹了哈爾濱工業(yè)大學(xué)等單位在超高強韌Mg-Gd-Y-Zn-Zr系變形鎂合金的規(guī);苽浜蛻(yīng)用方面的研究進展,并展望了Mg-Gd-Y-Zn-Zr系變形鎂合金的發(fā)展趨勢。
- Abstract:
-
The research and development of ultra-high strength and toughness magnesium alloys is of great significance to promote the application of magnesium alloys in high-tech industries. Magnesium and rare earth are the advantageous resources in China. The development of magnesium-rare earth (Mg-RE) alloys with ultra-high strength and toughness has unique advantages in China. Among them, Mg-Gd-Y-Zn-Zr wrought magnesium alloys can obtain ultra-high strength and ductility close to high-strength aluminum alloys, which have received great attention in recent years. In this paper, the effects of alloy composition, conventional plastic deformation processes, novel severe plastic deformation processes and heat treatment processes on the microstructure and mechanical properties of ultra-high strength and toughness Mg-Gd-Y-Zn-Zr wrought magnesium alloys are reviewed. The microstructure features, strengthening and toughening mechanisms of the Mg-Gd-Y-Zn-Zr wrought magnesium alloys with ultra-high strength and toughness are also discussed. The T5 peak-aging treated Mg-8-2Gd-3-8Y-1Zn-0-4Zr (mass fraction) extrusion alloy with ultra-high strength and toughness exhibits a “soft-hard” composite layered microstructure with bimodal grain sizes, and a near-continuous networks formed by precipitation of dense nanoscale basal and prismatic precipitates. The Mg-8-2Gd-3-8Y-1Zn-0-4Zr extrusion alloy obtains a tensile yield strength of 466 MPa, ultimate tensile strength of 514 MPa and elongation to failure of 145%. This paper also introduces the research progress of Harbin Institute of Technology and other groups in the largescale fabrication and application of ultrahigh strength and toughness Mg-Gd-Y-Zn-Zr wrought magnesium alloys, and the research trends on Mg-Gd-Y-Zn-Zr wrought alloys with ultra-high strength and toughness are also prospected.
備注/Memo
- 備注/Memo:
-
收稿日期:2019-08-29修回日期:2019-11-26 基金項目:國家重點研發(fā)計劃項目(2016YFB0301102);科技部“973”計劃項目(2013CB632200);科技部國際科技合作專題項目(2010DFB50210)第一作者:鄭明毅,男,1969年生,教授,博士生導(dǎo)師, Email: zhengmingyi_hit@126.com
更新日期/Last Update:
2020-01-06