Title:: The Influence of Cr Doping on the Flexural Strength and Microstructure of Sm2Co17 Type Sintered Permanent Magnet

Author(s):: LI Yu; YU Nengjun; LIU Bingyu; LIU lian; ZHANG Lin; GE Hongliang; 1.College of Materials and Chemistry, China Jiliang University, Hangzhou 310018, China 2.Mianyang Liangda Technology Innovation Service Co., Ltd,Mianyang 621000, China

Keywords:: Sm2Co17 type sintered permanent magnets; Cr doping; high flexural strength; microstructure; element distribution

CLC:

PACS:: TM273

DOI:: 10.7502/j.issn.1674-3962.202406013

DocumentCode:

Abstract:: The Sm2Co17 type sintered permanent magnets possess excellent magnetic properties, thermal stability and corrosion resistance. However, due to the primary 2∶17R phase crystal structure having few slip systems and poor symmetry, these permanent magnets exhibit relatively low flexural strength. This study investigated the effects of Cr element addition on the microstructure and flexural strength of Sm(Co0.68Fe0.22Cu0.06Zr0.04)7.5 sintered magnets. The research found that an appropriate amount of Cr addition can effectively enhance the flexural strength of the Sm2Co17 type sintered permanent magnets. When the Cr addition was 2wt%, the flexural strength of the magnet reached 180.12 MPa, which was about 47.75% higher than that of the magnet without Cr addition. Microstructure and elemental distribution analysis revealed that the Cr element is uniformly distributed within the magnet, having no significant impact on the phase composition and fracture mechanism of the magnet. However, the magnets with Cr addition formed fine irregular grains at the grain boundaries, and the size of the cellular structures within these fine grains was significantly smaller than that of the magnet without Cr addition. This resulted in a fine-grain strengthening effect, improving the flexural strength of the magnets. This study proposed a new method to enhance the flexural strength of Sm2Co17 type sintered magnets by inducing the formation of fine irregular grains and their internal fine cellular structures through the addition of Cr element, which helped optimize the performance of samariumcobalt magnets.

亚洲国产aⅴ成人精品无吗,中文字幕999精品,人妻人人妻a乱aa乱,日韩三级aaaaa,亚洲午夜成人精品无码色欲,国产第一页第二页av,老熟女北岛玲888av,99re热这里只有精品18,久久精品中文字幕久久

The Influence of Cr Doping on the Flexural Strength and Microstructure of Sm2Co17 Type Sintered Permanent Magnet(PDF)

MATERIALS CHINA[ISSN:1674-3962/CN:61-1473/TG]

Info

References

Memo

Common functions

Navigate

Tools

Statistics